miscibility and interactions in chitosan and polyacrylamide mixtures

MISCIBILITY AND INTERACTIONS IN CHITOSAN
AND POLYACRYLAMIDE MIXTURES
Katarzyna Lewandowska
Faculty of Chemistry
Nicolaus Copernicus University,
ul. Gagarina 7, 87-100 Toruń, Poland
e-mail: [email protected]
Abstract
In the present work, the results of Fourier transform infrared (FTIR) and atomic force microscopy
(AFM) studies of films of chitosan acetate (ChA), polyacrylamide (PAM), and their mixtures are
presented. The morphology of the ChA and PAM films and their mixtures was studied by tappingmode atomic force microscopy (AFM). The topography images were considered by determining
the root mean square (RMS) deviation in the image data. The study of mixtures by AFM showed
a completely different morphology when compared with pure components. The roughness
of mixtures increases with the increase of ChA content but is significantly reduced after UV
exposure. This may indicate a strong interaction between the polymeric components. The FTIR
spectroscopy also supports the obtained results. The miscibility of polymer mixtures is related to
interactions between the functional groups of the polymeric components.
Key words: chitosan, polyacrylamide, polymer blends, AFM, surface properties, FTIR analysis.
Progress on Chemistry and Application of Chitin and Its Derivatives, Volume XIX, 2014
DOI: 10.15259/PCACD.19.07
65
K. Lewandowska
1. Introduction
Polymer mixtures with biopolymers are widely used in biomedical applications. Chitosan (Ch), a deacetylated product of chitin, is a high molecular weight polysaccharide that
is mainly composed of β-(1→4)-2-amino-2-deoxy-D-glucopyranose units [1 - 3]. This biopolymer has good biocompatibility, biodegradation and bioactivity. Thus, chitosan has frequently been applied in medicine, pharmacy and the food industry. Polyacrylamide (PAM)
is a synthetic, non-ionic polymer that is soluble in water. This polymer is often combined
with other polymers [4 - 6]. In this paper, the mixtures composed of chitosan with polyacrylamide at different component ratios have been prepared as materials for various applications. The surface properties of polymer mixtures are important for their use in further
applications. UV-irradiation is a good way to modify the surface of polymeric materials,
with the surface structure of the polymeric films after modification being the result of photooxidation processes caused by exposure to ultraviolet radiation [7, 8].
The purpose of this study was to evaluate the interaction and miscibility of chitosan
acetate with polyacrylamide. The influence of UV-irradiation with a wavelength of 254 nm
on the surface properties of the homopolymers and their mixtures was also studied.
2. Materials and methods
2.1 Materials
The investigated systems contained chitosan (Ch) {degree of deacetylation DD = 78%,
Mv = 1.4×106 g/mol, Aldrich} mixed with polyacrylamide (PAM) {Mv = 2.5×10 6g/mol,
Aldrich}. Mixtures of chitosan with PAM samples were dissolved in 0.1 mol/dm3 acetic
acid. These solutions were cast to prepare the films. The films were dried in the vacuum
oven.
2.2 Methods
FTIR spectra of the used polymer samples and their blends were recorded on a Perkin
Elmer Spectrum 2000, in the wavelength range between 4000 – 400 cm-1, resolution of
2 cm-1 and 60-times scanning.
Topographic imaging was performed using a multimode scanning probe microscope
with a Nanoscope IIIa controller (Digital Instruments Santa Barbara, CA) operating in the
tapping mode, in air, at room temperature. Surface images, using scan widths ranging from
1 µm to 5 µm, with a scan rate of 1.97 Hz, were acquired at fixed resolution (512×512 data
points). Commercial silicon tips with spring constant 2 - 10 N/m were used. The roughness
parameter such as the root mean square (Rq) was calculated for the scanned area (1 × 1 µm)
using Nanoscope software. The AFM images and roughness calculations were obtained for
different sample places; the most typical areas are presented.
Thin polymeric films were irradiated in air at room temperature using a Philips TUV-300
mercury lamp which emits light mainly of wavelength 254 nm. Exposure time was 1 - 8 h.
66
Progress on Chemistry and Application of Chitin and Its Derivatives, Volume XIX, 2014
Miscibility and Interactions in Chitosan and Polyacrylamide Mixtures
3. Results and discussion
FTIR analysis has been used to identify interactions in polymer mixtures. Figure 1 presents the FTIR spectra of pure chitosan acetate and PAM before and after UV-irradiation.
The spectrum of chitosan acetate shows strong absorption bands at the frequency range
3300 - 3600 cm-1, the amide I absorption peaks at 1647 cm-1 and amide II at 1562 cm-1.
For the PAM sample, the FTIR spectrum also shows strong bands in the frequency range
3300 - 3600 cm-1, which are assigned to N-H stretching vibrations, and 1666 cm-1 (C=O
1,80
1,7
1,5
1079,78
3369,05
1,4
A)
1078,80
1077,96
3369,19
1,6
3368,49
1,3
1034,67
1034,19
1,2
1032,23
1562,17
1,1
1,0
A
0,9
0,8
Ch
0,7
Ch 2h
2883,47
2878,85
2877,84
Ch 8h
0,6
1568,76
2928,84
1566,02
1153,39
1153,32
1153,13
1414,99
1415,22
1379,71
1380,15
1646,78
0,5
1412,18
1649,88
655,42
618,57
619,56
659,55
618,52
660,05
1322,90
1321,94
1324,85
0,4
1655,88
0,3
898,95
898,92
898,82
1263,52
1261,69
2131,30
2131,38
2131,41
0,2
0,1
0,00
4000,0
3600
3200
2800
2400
2000
1800
cm-1
1600
1400
1200
1000
800
600
400,0
1,80
1,7
1662,96
1,6
1666,05
1662,77
B)
1,5
1,4
1,3
1,2
1,1
3356,78
1,0
A
3355,32
0,9
PAM
0,8
0,7
3347,46
0,6
0,5
0,4
1618,79
1618,91
3201,74
3200,55
PAM 2h
3202,41
1453,09
1452,39 1325,26
1324,38
1452,29
1418,69
1416,79
1419,44
1350,27
1322,73
1350,83
1349,58
PAM 8h
2936,16
2936,48
2936,59
0,3
1618,69
0,2
2147,01
2159,36
635,11
637,25
633,08
1125,51
1125,21
1124,87
1193,36
1192,18
1191,97
0,1
0,00
4000,0
3600
3200
2800
2400
2000
1800
cm-1
1600
1400
1200
1000
800
600
400,0
Figure 1. FTIR spectra of ChA and PAM before (A) and after (B) UV-irradiation.
Progress on Chemistry and Application of Chitin and Its Derivatives, Volume XIX, 2014
67
K. Lewandowska
3355,10
1666,39
3203,01
1618,29
1416,45
1452,29
1325,56
1350,85
2936,69
20/80
643,61
1091,37
3355,57
3204,84
1667,08
1562,07
1618,87
1412,34
1080,65
1027,85
2935,08
A
1345,61
651,59
1153,09
898,03
3360,43
50/50
1562,17
1666,20
1079,34
1029,86
1411,58
2932,19
1153,39
619,56
653,12
1326,14
1259,66
899,56
80/20
4000,0
3600
3200
2800
2400
2000
1800
cm-1
1600
1400
1200
1000
800
600
400,0
Figure 2. FTIR spectra of ChA/PAM mixtures.
2,01
1,9
1,8
1,7
1,6
1667,03
1666,78
1667,08
1,5
1,4
1,3
1,2
Oh
8h
1,1
A
1,0
0,9
3355,57
3355,95
3355,23
3204,84
3204,32
3202,35
1618,87
1618,78
1618,67
1561,22 1562,07
2h
0,8
1561,74
1412,34
1412,18
1079,11 1080,65
1077,05
1414,93
0,7
0,6
2935,08
2933,51
2934,72
0,5
1029,361027,85
1033,00
1345,61
0,4
651,59
650,14
651,06
1153,09
1152,92
1152,72
0,3
0,2
0,1
0,00
898,03
897,65
897,83
50/50
4000,0
3600
3200
2800
2400
2000
1800
cm-1
1600
1400
1200
1000
800
600
400,0
Figure 3. FTIR spectra of ChA/PAM (50/50) mixture before and after UV-irradiation.
stretching) [4]. In the film mixtures (Figure 2), the spectra are characterised by the presence of the absorption bands of the pure components, with intensity being approximately
proportional to the weight fraction of the component. Changes in the characteristic shape
of component spectra as well as small shifts in absorption peaks due to hydrogen bonding
between functional groups were observed.
68
Progress on Chemistry and Application of Chitin and Its Derivatives, Volume XIX, 2014
Miscibility and Interactions in Chitosan and Polyacrylamide Mixtures
UV-irradiation of samples causes systematic changes in their FTIR spectra (Figures 1
and 3). The main changes are observed in the frequency range of 3300 - 3600 cm-1 in
spectra of all irradiated samples. For the pure PAM and ChA/PAM mixtures, changes in the
1550 - 1700 cm-1 range were significantly smaller than for the ChA sample. Moreover, considering the relative changes in integral intensity bands, it can be concluded that mixtures
are more photostable than pure components.
The surface morphology results of films obtained for pure components and their mixtures before and after UV-irradiation are shown in Figures 4 - 6. Pure, un-irradiated PAM
film has the smoothest surface. This agrees with the value of the roughness parameter, which
is about 0.6 nm (Table 1). For the pure, un-irradiated ChA film, the surface morphology
is characterised by a more corrugated surface, with the roughness parameter being about
3 times higher than that for PAM film.
In the case of ChA/PAM mixtures (Figure 6), the surface topology began to alter. The
AFM image (Figure 6) illustrates the decreasing number and height of peaks on the film
surface. The surface becomes more flat. The observed changes in morphology are related
to the interactions between polymeric compounds. UV-irradiation causes modification of
all surfaces. The film surfaces become smoother after UV-irradiation and the values of the
A)
B)
Figure 4. AFM images of the surface of chitosan films before UV irradiation (A) and after 8 h of
UV irradiation (B).
A)
B)
Figure 5. AFM images of the surface of PAM films before UV irradiation (A) and after 8 h of UV
irradiation (B).
Progress on Chemistry and Application of Chitin and Its Derivatives, Volume XIX, 2014
69
K. Lewandowska
A)
B)
Figure 6. AFM images of the surface of ChA/PAM mixture (50/50) films before UV irradiation
(A) and after 8 h of UV irradiation (B).
Table 1. The roughness parameters (Rq) for films of ChA/PAM mixtures of different composition
before and after 8 h of UV irradiation. wChA – the weight fraction of chitosan.
wChA
Rq [nm]
0h
8h
0.0
0.55
0.29
0.5
1.20
0.70
1.0
1.80
1.40
roughness parameters decrease (Table 1). Such changes in surface morphology may result
from various photo-oxidation, photodegradation and photocross-linking reactions occurring
in the polymeric samples.
4. Conclusions
1. FTIR analysis showed the existence of a weak interaction of the hydroxyl or amino
groups of chitosan with the amide groups of PAM. 2. The interactions between chitosan and PAM macromolecules in the mixtures, including hydrogen bonds, led to the protection of surfaces against
UV-treatment.
3. The surface of PAM is flat; it has the lowest values for the roughness parameter.
4. AFM images show differences in surface properties of PAM films, and films made
of mixture of chitosan and PAM.
5. The surface roughness of mixtures increases with the increase in ChA content.
6. The surface of chitosan and PAM films and their mixtures are altered by UV-irradiation.
7. The surface roughness of chitosan and ChA/PAM mixture films is reduced as a result
of exposure to UV light.
5. References
1. Rinaudo M; (2008) Review, Main properties and current applications of some polysaccharides as biomaterials. Polym Int 57, 397-430, DOI: 10.1002/pi.2378.
70
Progress on Chemistry and Application of Chitin and Its Derivatives, Volume XIX, 2014
Miscibility and Interactions in Chitosan and Polyacrylamide Mixtures
2. Sionkowska A; (2011) Current research on the blends of natural and synthetic polymers: review. Prog
Polym Sci 36, 1254-1276, DOI: 10.1016/j.progpolymsci.2011.05.003.
3. Lewandowska K; (2012) Surface studies of microcrystalline chitosan/poly(vinyl alcohol) mixtures. App
Surf Sci 263,115-123, DOI: 10.1016/j.apsusc.2012.09.011.
4. Xiao Ch, Lu Y, Jing Z, Zhang L; (2002) Study on physical properties of blend films from gelatine and
polyacrylamide solutions. J Appl Polym Sci 83, 949-955, DOI: 10.1002/app.2274.
5. Lewandowska K., (2012) Progress on Chemistry and Application of Chitin and Its Derivatives, Monograph, Vol. XVII, Polish Chitin Society, In: Jaworska M. (ed), Lodz, pp. 53-58.
6. Li R, Xiong Ch, Dong L; (2011) Preparation of the high dielectric performance flexible materials
achieved by polyacrylamide/poly(vinylidene fluoride) blends. e-Polymers 11, 892-897, DOI: 10.1515/
epoly.2011.11.1.892.
7. Zhang Z, Peng J, Huang L, Zhai M, Li J, Wei G; (2006) Studies on radiation degradation of chitosan in
aqueous solutions. Acta Polym Sin 7, 841-847.
8. Sionkowska A, Skopinska-Wisniewska J, Planecka A, Kozlowska J; (2010) The influence of UV irradiation on the properties of chitosan films containing keratin. Polym Deg Stab 95, 2486-2491, DOI:
10.1016/j.polymdegradstab.2010.08.002.
Progress on Chemistry and Application of Chitin and Its Derivatives, Volume XIX, 2014
71
K. Lewandowska
72
Progress on Chemistry and Application of Chitin and Its Derivatives, Volume XIX, 2014